| LIANG Qiang,XU Yonghang,DU Yanbin,WANG Jing,XU Binyuan.Optimization Method of Laser Polishing Process Parameters for D2 Steel Based on Comprehensive Satisfaction Function[J],53(16):169-181 |
| Optimization Method of Laser Polishing Process Parameters for D2 Steel Based on Comprehensive Satisfaction Function |
| Received:October 31, 2023 Revised:December 24, 2023 |
| View Full Text View/Add Comment Download reader |
| DOI：10.16490/j.cnki.issn.1001-3660.2024.16.014 |
| KeyWord:D2 steel laser polishing process parameter optimization comprehensive satisfaction function dual-response surface model comprehensive entropy weight |
| Author | Institution |
| LIANG Qiang |
College of Mechanical Engineering, Chongqing Technology and Business University, Chongqing , China;Chongqing Key Laboratory of Green Design and Manufacturing of Intelligent Equipment, Chongqing Technology and Business University, Chongqing , China |
| XU Yonghang |
College of Mechanical Engineering, Chongqing Technology and Business University, Chongqing , China |
| DU Yanbin |
College of Mechanical Engineering, Chongqing Technology and Business University, Chongqing , China;Chongqing Key Laboratory of Green Design and Manufacturing of Intelligent Equipment, Chongqing Technology and Business University, Chongqing , China |
| WANG Jing |
College of Mechanical Engineering, Chongqing Technology and Business University, Chongqing , China;Chongqing Key Laboratory of Green Design and Manufacturing of Intelligent Equipment, Chongqing Technology and Business University, Chongqing , China |
| XU Binyuan |
College of Mechanical Engineering, Chongqing Technology and Business University, Chongqing , China |
|
| Hits: |
| Download times: |
| Abstract: |
| Due to its excellent wear resistance and good workability, D2 steel is widely used in various cold work moulds. However, after long time working, the roughness of D2 die steel on the surface of the die will be greatly increased, which will seriously affect the precision of the products. Laser polishing technology, as a non-contact, stable and easily automated surface treatment technology, can effectively reduce the roughness of the material surface. However, in the laser polishing process, due to the laser beam working back and forth, the roughness or hardness of the polished overlap or corners, etc. will be unstable compared with the unpolished part. How to control this instability, so that the whole laser polished part of the various values tend to stabilize, there are still few research reports. Therefore, in order to simultaneously improve the laser polishing effect and the stability of the polishing quality of D2 die steel, a method for optimizing the laser polishing process parameters of D2 steel based on the comprehensive satisfaction function was proposed. Firstly, a continuous laser was used for laser polishing based on the Box-Behnken method for a 3-factor, 3-level experimental design with surface roughness, microhardness and polishing depth as the optimization objectives, and laser power, scanning speed and overlap rate as the experimental factors. Secondly, the dual-response surface model of the mean value and standard deviation of each objective was constructed according to the experimental data, and the objective entropy weight of the mean value and standard deviation of each objective was obtained according to the entropy weight theory, and the comprehensive entropy weight was constructed in combination with the subjective entropy weight. Finally, the dual-response surface model and comprehensive entropy right were introduced into the satisfaction function to construct an improved comprehensive satisfaction model, and the optimal combination of process parameters was obtained according to the stochastic gradient descent method, which was compared with the optimized dual-response surface method to prove the superiority of the method. The experimental results showed that with the laser power of 551 W, the scanning speed of 9 mm/s, and the overlap rate of 0.55, the roughness decreased from Ra=5.188 μm to Ra=1.056 μm with a reduction of 79.65% and the standard deviation of the roughness was 0.012 8 μm. The microhardness decreased from 541.3HV0.5 to 509.3HV0.5 with a reduction of 5.91% and the standard deviation of microhardness was 12.981 1HV0.5. At the same time, the depth of polishing was 0.331 mm and the standard deviation of the depth of polishing was 0.002 4 mm. Comparison of the comprehensive results of the improved comprehensive satisfaction model method with the dual-response surface method, combining with the results of the friction wear experiments after the optimal combination of process parameters and traditional mechanical polishing, shows that the method proposed in this paper can maximize the microhardness while effectively reducing the surface roughness, keeping the polishing depth as small as possible. This method can provide a reference for the optimization of laser polishing process parameters for D2 die steel. |