| ZENG Fan-yong,LI Yang-liang,ZHANG De-qin,LI Hai-zhou,PAN Dong,NI Xiao-feng.Study on the tensile strength of B82MnQL materials by hot dip galvanizing[J],45(3):96-102 |
| Study on the tensile strength of B82MnQL materials by hot dip galvanizing |
| Received:November 16, 2015 Revised:March 20, 2016 |
| View Full Text View/Add Comment Download reader |
| DOI：10.16490/j.cnki.issn.1001-3660.2016.03.016 |
| KeyWord:B82MnQL wire rod drawing galvanized galvanizing steel wire stabilization treatment tensile strength |
| Author | Institution |
| ZENG Fan-yong |
School of Mechanical and Materials Engineering, Jiujiang University, Jiujiang , China |
| LI Yang-liang |
School of Mechanical and Materials Engineering, Jiujiang University, Jiujiang , China |
| ZHANG De-qin |
School of Mechanical and Materials Engineering, Jiujiang University, Jiujiang , China |
| LI Hai-zhou |
School of Mechanical and Materials Engineering, Jiujiang University, Jiujiang , China |
| PAN Dong |
School of Mechanical and Materials Engineering, Jiujiang University, Jiujiang , China |
| NI Xiao-feng |
Ossen Innovation Materials Co. , Ltd, Jiujiang , China |
|
| Hits: |
| Download times: |
| Abstract: |
| The B82MnQL wire rod for used as the material for hot dip galvanizing experiment, using tensile testing machine, repeated bending testing machine on the mechanical properties were tested。The microstructure of the cross section、the axial section and the drawing fracture were analyzed by means of optical microscope and scanning electron microscope.The results show：The B82MnQL wire rod tensile strength increased from 1250MPa to 1670MPa.The shrinkage rate of the cross section decreased from 32.5% to 7%.Used the new technology and the formula of the assistant plating,the tensile strength of the B82MnQL steel wire after galvanized was decreased by 8%,lower than traditional 10-15%. After stabilization , the B82MnQL"s torsion value about 20 times, repeated bending about 6 times, strength increased from 1710MPa to 1650MPa, The hardness value is higher than that of the galvanized, raised from 430HV to 450HV, and uniformly dispersed. |