龚云柏,王平,杨彪,伍婷,杨钊,段艳菲,兰欣悦.热输入对TC4钛合金微弧氧化膜层性能的影响[J].表面技术,2022,51(12):159-168.
GONG Yun-bai,WANG Ping,YANG Biao,WU Ting,YANG Zhao,DUAN Yan-fei,LAN Xin-yue.Effects of Heat Input on Characteristics of Micro-arc Oxidation Coatings on TC4 Titanium Alloy[J].Surface Technology,2022,51(12):159-168
热输入对TC4钛合金微弧氧化膜层性能的影响
Effects of Heat Input on Characteristics of Micro-arc Oxidation Coatings on TC4 Titanium Alloy
  
DOI:10.16490/j.cnki.issn.1001-3660.2022.12.016
中文关键词:  TC4钛合金  微弧氧化  热输入  微观结构  耐腐蚀性  耐磨性
英文关键词:TC4 titaninum alloy  micro-arc oxidation  heat input  microstructure  corrosion resistance  wear resistance
基金项目:四川省科技计划(2022YFSY0018)
作者单位
龚云柏 西南石油大学 新能源与材料学院,成都 610500 
王平 西南石油大学 新能源与材料学院,成都 610500 
杨彪 西南石油大学 新能源与材料学院,成都 610500 
伍婷 亥姆霍兹HEREON材料与海岸研究中心,盖斯特哈赫特 21502 
杨钊 西南石油大学 新能源与材料学院,成都 610500 
段艳菲 西南石油大学 新能源与材料学院,成都 610500 
兰欣悦 西南石油大学 新能源与材料学院,成都 610500 
AuthorInstitution
GONG Yun-bai School of New Energy and Materials, Southwest Petroleum University, Chengdu 610500, China 
WANG Ping School of New Energy and Materials, Southwest Petroleum University, Chengdu 610500, China 
YANG Biao School of New Energy and Materials, Southwest Petroleum University, Chengdu 610500, China 
WU Ting Institute of Surface Science, Helmhotz-Zentrum Hereon, Geesthacht 21502, Germany 
YANG Zhao School of New Energy and Materials, Southwest Petroleum University, Chengdu 610500, China 
DUAN Yan-fei School of New Energy and Materials, Southwest Petroleum University, Chengdu 610500, China 
LAN Xin-yue School of New Energy and Materials, Southwest Petroleum University, Chengdu 610500, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 研究热输入对TC4钛合金微弧氧化膜层性能的影响,控制微弧氧化过程中的能量消耗。方法 在TC4钛合金表面制备微弧氧化膜层时,通过改变热输入来形成不同的热效应,采用扫描电镜、能谱仪、X射线衍射仪分析在不同热输入下所制备膜层的表面形貌、截面形貌、元素分布和相组成,测试热输入对TC4钛合金微弧氧化膜层耐磨性和耐蚀性的影响。结果 热输入影响了膜层生成过程中的离子传输,提高了膜层中Ti原子与O原子的比值,有利于TiO2膜层的生成,但过高的热输入会使参与反应的Ti、O原子减少,从而降低膜层的生长速率。膜层的厚度随着热输入的增大先由18.53 μm增加至21.56 μm,随后减小至17.67 μm,膜层主要相的组成为Rutile、Anatase及少量SiO2。通过改变热输入提高了膜层的耐腐蚀性能,其腐蚀速率从4.516×10–3 mm/a逐渐减小至3.109×10–4 mm/a。膜层表面的耐磨性能随着热输入的增大呈先增加后降低的趋势。结论 当热输入为140 W时,膜层的厚度最高,耐磨性能最佳,同时具备良好的耐腐蚀性能。
英文摘要:
      Micro-arc oxidation technology is an environmentally friendly surface modification technology, which improves the surface properties such as wear resistance, corrosion resistance, thermal shock resistance, hardness and other properties by in-situ synthesis of functional ceramic coatings on the valve metal surface. Some scholars have found that during the micro-arc oxidation process, a large amount of heat is released, the temperature of the electrolyte increases rapidly, which seriously affects the corrosion resistance and wear resistance of the coating. The work aims to study the effects of heat input on the characteristics of the micro-arc oxidation coating of TC4 titanium alloy by adjusting the heater power so as to provide a theoretical basis for improving the refrigeration system in micro-arc oxidation. The TC4 titanium alloy was cut into a rectangle of 15 mm×15 mm×2 mm as the base material and polished and with 400#, 800#, 1200#, 2000# sandpaper in turn. The test adopted pulse power supplies (DWL20-6), the output mode adopted constant current, the current density was 5.2 A/dm2, the frequency was 100 Hz, the duty cycle was 40%, and the time was 15 min. The electrolyte composition was Na2SiO3 (12 g/L), (NaPO3)6 6 g/L, Na2WO4 1.5 g/L, NaOH 0.5 g/L, C3H8O3 3 mL/L, EDTA 0.3 g/L, C6H15NO3 1 mL/L. Before the test, the initial temperature was controlled to 20 ℃ by the cool system, the constant heat input during the micro-arc oxidation process was controlled to 0, 70, 140, 210, 280 W respectively. The surface morphology, cross-sectional morphology and elements of the coatings were analyzed by scanning electron microscopy (ZEISS EVO MA15) and X-ray energy dispersive spectrometer (OXFORD X-max). The phase composition of the coatings was analyzed by X-ray diffractometer (DX-2700B). The microhardness of the coating was measured by a digital microhardness tester (HXD- 2000TM/LCD, China). The polarization curves of the solution samples against 3.5wt.% NaCl solution were measured using an electrochemical workstation (Gamry Reference 3000, USA). Reciprocating friction using a multifunctional material surface property testing machine (MFT-4000). With the increase of heat input, the coating thickness increased first and then decreased. The main phases of the coating were Rutile TiO2, Anatase TiO2 and a small amount of SiO2. The heat input improved the corrosion resistance of the coating, and the corrosion rate gradually decreased from 4.516×10–3 mm/a to 3.109×10–4 mm/a. The wear resistance of the coating surface first increased and then decreased with the increase of heat input. When the constant heat input was 140 W, the TC4 titaniumalloy micro-arc oxidation coating had the best comprehensive performance, its thickness was 21.56 μm, the surface roughness RA was 1.47 μm, and it had good corrosion resistance and wear resistance. The heat input affected the ion transport during the formation of the coating, and increased the ratio of Ti atoms to O atoms in the coating, which was beneficial to the formation of the TiO2 coating. Get rid of the bondage, the Ti and O atoms participating in the reaction were reduced, and the growth rate of the coating was reduced. The coating thickness increased from 18.53 μm to 21.56 μm and then decreased to 17.67 μm with the heat input. The main phases of the coating were Rutile, Anatase and a small amount of SiO2. By controlling the external heat input, the structure of the TC4 titanium alloy micro-arc oxidation coating can be improved, and the performance of the coating can be improved.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第23672585位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号