张春霖,张丽,李胜利,李静,张诗涵,解志文.不同预热温度WC增强镍基合金堆焊层的微结构演化与摩擦学性能[J].表面技术,2024,53(9):127-136.
ZHANG Chunlin,ZHANG Li,LI Shengli,LI Jing,ZHANG Shihan,XIE Zhiwen.Microstructure Evolution and Tribological Property of WC Reinforced Nickel Based Alloy Surfacing Layer Fabricated at Different Preheating Temperature[J].Surface Technology,2024,53(9):127-136 |
| 不同预热温度WC增强镍基合金堆焊层的微结构演化与摩擦学性能 |
| Microstructure Evolution and Tribological Property of WC Reinforced Nickel Based Alloy Surfacing Layer Fabricated at Different Preheating Temperature |
| 投稿时间：2023-04-12 修订日期：2023-10-23 |
| DOI：10.16490/j.cnki.issn.1001-3660.2024.09.012 |
| 中文关键词: 预热温度 等离子堆焊 镍基WC涂层 微观组织 磨损机理 |
| 英文关键词:preheating temperature PTAW Nickel based WC layer microstructure wear mechanisms |
| 基金项目:国家重点研发计划(2021YFB3702003) |
|
|
| Author | Institution |
| ZHANG Chunlin | School of Materials and Metallurgy,Liaoning Anshan 114051, China |
| ZHANG Li | School of Materials and Metallurgy,Liaoning Anshan 114051, China |
| LI Shengli | School of Materials and Metallurgy,Liaoning Anshan 114051, China |
| LI Jing | School of Mechanical Engineering and Automation, University of Science and Technology Liaoning, Liaoning Anshan 114051, China |
| ZHANG Shihan | School of Mechanical Engineering and Automation, University of Science and Technology Liaoning, Liaoning Anshan 114051, China |
| XIE Zhiwen | School of Mechanical Engineering and Automation, University of Science and Technology Liaoning, Liaoning Anshan 114051, China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 研究不同预热温度(200、400 ℃)条件下硬质颗粒增强镍基合金堆焊层的微观组织结构演化机理，以及对其力学性能、磨损性能的影响规律。方法 采用等离子弧焊接技术在42CrMo钢基体表面堆焊硬质WC颗粒增强镍基强化层，利用X射线衍射(XRD)、扫描电子显微镜(SEM)、硬度计和摩擦磨损试验机，分析不同预热温度堆焊层的物相组成、微观组织形貌、力学性能和磨损性能，建立堆焊层制备工艺–微观组织结构–力学性能–磨损性能之间的强映射关系。结果 堆焊层主要由γ-Ni/Fe、WC、W2C、M7C3、M23C6、Ni2W4C、Cr3C2等物相组成，在预热温度200 ℃下堆焊层二次碳化物析出较少，发生了严重的WC颗粒沉降现象;在预热温度400 ℃下，堆焊层析出了大量的二次碳化物，WC颗粒沉降减弱，组织均匀性提高。在400 ℃下预热，相较于200 ℃下预热，堆焊层的磨损质量减少了51.85%，磨损率减少了51.89%。结论 高预热温度和长保温时间可促进WC颗粒界面反应，驱动大面积二次碳化物的析出，有效缓解WC颗粒沉降，改善凝固组织中WC颗粒的分布均匀性，从而显著提高堆焊层的硬度和耐磨性。 |
| 英文摘要: |
| Components in severe environment often fail to work due to abrasion, corrosion and fractures, surface strengthening technology has important applications in the fields of aerospace, steel and metallurgy. Nickel-WC is an ideal coating material for improving both wear resistance and corrosion resistance of components surfaces. However, WC bottom–concentrated situation generally occurs owning to large density of WC particles (16.5 g/cm3), which can cause stress concentration and increase the risk of cracking. WC bottom–concentrated situation is not desired in the fabricated process. In this study, WC particles reinforced Nickel alloy layers were prepared with different preheating schedule on 42CrMo steel substrate by powder plasma arc welding technology. The work aims to demonstrate the microstructure evolution of hard particle reinforced Nickel based alloy surfacing layers at different preheating temperature (200 ℃ and 400 ℃) and investigate the effects on the mechanical and tribology properties. |