朱鹏飞,严宏志,陈志,吴顺兴,张慧.渗碳齿轮齿根喷丸强化研究现状与展望[J].表面技术,2021,50(1):10-27, 46.
ZHU Peng-fei,YAN Hong-zhi,CHEN Zhi,WU Shun-xing,ZHANG Hui.Research Status and Prospect of Shot Peening for Carburized Gear Roots[J].Surface Technology,2021,50(1):10-27, 46
渗碳齿轮齿根喷丸强化研究现状与展望
Research Status and Prospect of Shot Peening for Carburized Gear Roots
投稿时间:2020-08-18  修订日期:2020-12-11
DOI:10.16490/j.cnki.issn.1001-3660.2021.01.002
中文关键词:  齿根  弯曲疲劳  喷丸  表面完整性  裂纹
英文关键词:gear root  bending fatigue  shot peening  surface integrity  crack
基金项目:国家自然科学基金项目(52075552);湖南省创新创业技术投资项目(2019GK5032)
作者单位
朱鹏飞 中南大学,长沙 410083;开封大学,河南 开封 475004 
严宏志 中南大学,长沙 410083 
陈志 中南大学,长沙 410083 
吴顺兴 中南大学,长沙 410083 
张慧 中南大学,长沙 410083 
AuthorInstitution
ZHU Peng-fei Central South University, Changsha 410083, China;Kaifeng University, Kaifeng 475004, China 
YAN Hong-zhi Central South University, Changsha 410083, China 
CHEN Zhi Central South University, Changsha 410083, China 
WU Shun-xing Central South University, Changsha 410083, China 
ZHANG Hui Central South University, Changsha 410083, China 
摘要点击次数:
全文下载次数:
中文摘要:
      弯曲疲劳是齿轮传动中的主要失效形式,严重影响了齿轮使用性能。喷丸强化工艺是齿轮常用的表面强化方法,对提升齿根抗弯曲疲劳性能效果显著。介绍了两种典型的喷丸强化方法(气动式喷丸和离心式喷丸),分别从应用范围、加工效率、喷射原理、表面完整性等方面对其进行了比较。为揭示喷丸强化机制,概述了喷丸工艺数值模拟与工艺参数优化方法,分析了喷丸对齿根表面完整性影响机制,并阐述了表面完整性参量之间的相互作用关系。同时,阐明了齿轮喷丸后的疲劳断裂机理,包括裂纹萌生与扩展机制。在此基础上,重点论述了受喷齿轮弯曲疲劳性能的影响因素,并提出了改善齿轮疲劳强度的措施。此外,简要探讨了齿轮喷丸后,疲劳强度提升幅度问题,并归纳了受喷齿轮弯曲疲劳建模方法。最后,对齿轮齿根喷丸强化工艺进行总结,并对其发展趋势进行了展望。
英文摘要:
      Bending fatigue is the main failure form of gear transmission, which seriously affects the service performance of gears. Shot peening strengthening technology is a common surface strengthening method for gears that can effectively improve the bending fatigue resistance for gear roots. Two typical shot peening strengthening methods (air-blast peening and centrifugal peening) were introduced, which were compared from the aspects of application range, machining efficiency, spraying principle, surface integrity, etc., respectively. To reveal the mechanism of shot peening strengthening, numerical simulation and parameter optimization methods of shot peening were summarized, influence mechanism of shot peening on the surface integrity of gear roots was analyzed, and correlation of surface integrity parameters was expounded. Meanwhile, the fatigue fracture mechanism (including crack initiation and propagation) of shot-peened gears were revealed. On this basis, influence factors of bending fatigue for shot-peened gears were emphatically discussed, and measures to improve the fatigue strength of gears were put forward. In addition, the gain in fatigue strength of shot-peened gear was discussed briefly, and bending fatigue modeling methods for shot-peened gears were generalized. Finally, shot-peening strengthening process of gear roots was summarized and its development trend was prospected.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第24187069位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号