王栋,律谱,陈真真.三维表面粗糙度对18CrNiMo7-6 钢旋转弯曲疲劳寿命的影响[J].表面技术,2019,48(11):283-289.
WANG Dong,LYU Pu,CHEN Zhen-zhen.Effect of Three-dimensional Surface Roughness on Rotating Bending Fatigue Life of 18CrNiMo7-6 Steel[J].Surface Technology,2019,48(11):283-289
三维表面粗糙度对18CrNiMo7-6 钢旋转弯曲疲劳寿命的影响
Effect of Three-dimensional Surface Roughness on Rotating Bending Fatigue Life of 18CrNiMo7-6 Steel
投稿时间:2019-01-16  修订日期:2019-11-20
DOI:10.16490/j.cnki.issn.1001-3660.2019.11.031
中文关键词:  三维粗糙度  疲劳寿命  旋转弯曲疲劳  三维表面形貌特征  18CrNiMo7-6钢  纹理方向
英文关键词:3-D roughness, fatigue life  rotating bending fatigue  three-dimensional surface topography  18CrNiMo7-6 steel  texture direction
基金项目:国家自然科学基金项目(U1804254)
作者单位
王栋 郑州大学 a.机械与动力工程学院 b.河南省资源与材料工业技术研究院,郑州 450001 
律谱 郑州大学 b.河南省资源与材料工业技术研究院,郑州 450001 
陈真真 郑州大学 a.机械与动力工程学院,郑州 450001 
AuthorInstitution
WANG Dong a.School of Mechanical and Power Engineering, b.Henan Province Industry Technology Research Institute of Resources and Materials, Zhengzhou University, Zhengzhou 450001, China 
LYU Pu b.Henan Province Industry Technology Research Institute of Resources and Materials, Zhengzhou University, Zhengzhou 450001, China 
CHEN Zhen-zhen a.School of Mechanical and Power Engineering, Zhengzhou University, Zhengzhou 450001, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 探究固定载荷下三维表面粗糙度Sa对18CrNiMo7-6钢旋转弯曲疲劳寿命的影响。方法 通过砂纸研磨制备不同表面粗糙度及纹理方向的18CrNiMo7-6钢旋转弯曲疲劳试样,测量所有试样的表面粗糙度参数Sa及三维表面形貌参数Sq、Sz、Ssk、Sku。对试样进行旋转弯曲疲劳试验,分析疲劳寿命。结果 在相同或相近粗糙度的情况下,轴向纹理疲劳试样疲劳寿命大于周向纹理疲劳试样疲劳寿命。相同纹理方向的情况下,表面三维粗糙度Sa越低,试样疲劳寿命越高。试样疲劳寿命次数与表面粗糙度参数Sa及三维表面形貌参数Sq、Sz、Ssk、Sku均有明显的相关性。结论 对于18CrNiMo7-6钢旋转弯曲疲劳试样,拥有平行于疲劳应力的机械加工纹理比垂直于疲劳应力的机械加工纹理具有更小的危害性。降低18CrNiMo7-6试样表面粗糙度,能够有效提高试样旋转弯曲疲劳寿命。纹理方向平行于疲劳应力方向的试样,表面偏斜度Ssk对零件疲劳寿命影响不明显。
英文摘要:
      The work aims to explore the effect of three-dimensional surface roughness Sa on the bending fatigue life of 18CrNiMo7-6 steel under the fixed load. 18CrNiMo7-6 steel rotating bending fatigue specimens with different surface roughness and texture path were prepared by sandpaper grinding. The surface roughness parameters Sa and three-dimensional surface topography parameters Sq, Sz, Ssk, and Sku of all specimens were measured. Rotational bending fatigue test was carried out on the specimen to analyze the fatigue life of the specimen. The fatigue life of axial textured specimens with the same or similar roughness was greater than that of circumferential textured specimens. Under the same texture direction, the lower the three- dimensional surface roughness was, the higher the fatigue life was. The fatigue life times of specimens were significantly correlated with Sa and Sq, Sz, Ssk, and Sku. For 18CrNiMo7-6 steel rotating bending fatigue specimens, machining grooves perpendicular to fatigue stress are more harmful than machining grooves parallel to fatigue stress. Reducing the surface roughness of the 18CrNiMo7-6 steel specimen can effectively improve the rotational bending fatigue life of the specimen. The surface skewness Ssk of the specimen with texture direction parallel to the fatigue stress direction has no obvious influence on the fatigue life of the part.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第24082340位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号