孙俊杰,邓重启,屈臣鸣,王文涛.纯水射流间接强化对18CrNiMo7-6钢表面粗糙度和残余应力的影响[J].表面技术,2018,47(7):173-178.
SUN Jun-jie,DENG Chong-qi,QU Chen-ming,WANG Wen-tao.Effects of Indirect Strengthening by Pure Water Jet on Surface Roughness and Residual Stress of 18CrNiMo7-6 Steel[J].Surface Technology,2018,47(7):173-178
纯水射流间接强化对18CrNiMo7-6钢表面粗糙度和残余应力的影响
Effects of Indirect Strengthening by Pure Water Jet on Surface Roughness and Residual Stress of 18CrNiMo7-6 Steel
投稿时间:2018-03-23  修订日期:2018-07-20
DOI:10.16490/j.cnki.issn.1001-3660.2018.07.024
中文关键词:  水射流  喷射压力  喷射靶距  钢珠直径  粗糙度  残余压应力
英文关键词:water jet  injection pressure  jet target distance  steel ball diameter  roughness  residual compressive stress
基金项目:
作者单位
孙俊杰 郑州大学 机械工程学院,郑州 450001 
邓重启 郑州大学 机械工程学院,郑州 450001 
屈臣鸣 郑州大学 机械工程学院,郑州 450001 
王文涛 郑州大学 机械工程学院,郑州 450001 
AuthorInstitution
SUN Jun-jie School of Mechanical Engineering, Zhengzhou University, Zhengzhou 450001, China 
DENG Chong-qi School of Mechanical Engineering, Zhengzhou University, Zhengzhou 450001, China 
QU Chen-ming School of Mechanical Engineering, Zhengzhou University, Zhengzhou 450001, China 
WANG Wen-tao School of Mechanical Engineering, Zhengzhou University, Zhengzhou 450001, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 减小高压水射流强化中冲蚀现象对材料表面的影响。方法 选择水射流喷射压力、喷射靶距和覆盖小钢珠直径为可变参数,对18CrNiMo7-6渗碳合金钢进行高压水射流强化单因素试验。运用三维表面形貌测量系统和X射线残余应力分析仪对试验后的材料进行测量分析。结果 随着压力的增大,表面粗糙度增加,残余应力最大可达693 MPa,但继续增大喷射压力反而会使残余压应力减小。随着靶距的增加,表面残余应力几乎直线减小,表面粗糙度则在靶距为110 mm时达到最小值0.77 μm。随着小钢珠直径的增加,表面残余压应力先增大后减小,最大值为782 MPa;表面粗糙度先变小后增大,最小值为0.76 μm。结论 水射流喷射压力、喷射靶距和覆盖小钢珠直径对18CrNiMo7-6钢的表面粗糙度和残余应力影响明显。同时,每个参数在不同的变化范围,对材料表面主要的影响方式不同,对材料的表面粗糙度和表面残余压应力的影响也存在着差异。
英文摘要:
      The work aims to reduce the effects of erosion phenomenon on material surface in high-pressure water jet strengthening technology. Single factor test was applied to 18CrNiMo7-6 carburizing alloy steel by selecting water jet pressure, jet target distance and covering small steel ball diameter as variable parameters. The tested materials were measured and analyzed by means of three dimensional surface morphology measurement system and X-ray residual stress analyzer. Surface roughness increased as the pressure increased, and the maximum residual stress was 693 MPa. However, residual compressive stress decreased as injection pressure further increased. With the increase of target distance, surface residual stress decreased almost linearly, the surface roughness reached the minimum value of 0.77 μm at the target distance of 110 mm. As small steel ball diameter increased, the surface residual compressive stress first increased and then decreased, and the maximum value was 782 MPa; the surface roughness first decreased and then increased, and the minimum value was 0.76 μm. Both surface roughness and residual stress of 18CrNiMo7-6 steel are obviously affected by water jet injection pressure, injection target distance and covering small steel ball diameter. Meanwhile, each parameter has different influence mode on material surface in different variation range, and different influence on surface roughness and residual compressive stress of materials.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第24160555位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号