杨振凯,王海军,刘明,王晶晨.基于响应曲面法的 Ar-N2 等离子射流特性研究[J].表面技术,2016,45(1):148-154,160.
YANG Zhen-kai,WANG Hai-jun,LIU Ming,WANG Jing-chen.Characteristics of the Ar-N2 Plasma Jet by Response Surface Methodology[J].Surface Technology,2016,45(1):148-154,160
基于响应曲面法的 Ar-N2 等离子射流特性研究
Characteristics of the Ar-N2 Plasma Jet by Response Surface Methodology
投稿时间:2015-09-20  修订日期:2016-01-20
DOI:10.16490/j.cnki.issn.1001-3660.2016.01.024
中文关键词:  超音速等离子喷涂  AT40  射流特性  响应曲面法
英文关键词:supersonic plasma spraying  AT40 coating  plasma jet characteristics  response surface methodology
基金项目:国家自然科学基金项目(51175513)
作者单位
杨振凯 装甲兵工程学院 装备再制造技术国防科技重点实验室, 北京 100072 
王海军 装甲兵工程学院 装备再制造技术国防科技重点实验室, 北京 100072 
刘明 装甲兵工程学院 装备再制造技术国防科技重点实验室, 北京 100072 
王晶晨 1. 装甲兵工程学院 装备再制造技术国防科技重点实验室, 北京 100072;2. 河北工业大学 材料科学与工程学院, 天津 300130 
AuthorInstitution
YANG Zhen-kai National Key Lab for Remanufacturing, Academy of Armored Forces Engineering, Beijing 100072, China 
WANG Hai-jun National Key Lab for Remanufacturing, Academy of Armored Forces Engineering, Beijing 100072, China 
LIU Ming National Key Lab for Remanufacturing, Academy of Armored Forces Engineering, Beijing 100072, China 
WANG Jing-chen 1. National Key Lab for Remanufacturing, Academy of Armored Forces Engineering, Beijing 100072, China;2. School of Materials Science and Engineering, Hebei University of Technology, Tianjin 300130, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 研究等离子射流特性,提高射流品质,为工程实践提供支撑。 方法 通过响应曲面法,以粒子速度和温度为指标反映射流特性的变化,采用 Box-Behnken-Design (BBD)设计分析电流(I)、主气流量(Q)以及次级气比例(C)对于射流特性的影响规律及其相互作用关系。 结果 对粒子速度的影响因素排序为 QAr>I>C,对粒子温度的影响因素排序为 I>QAr>C。 该喷嘴下实现最佳加热效应的参数为:主气流量 80 L/ min、电流 450 A、次级气比例 22. 5% 。 实现射流最佳加速效应的离子气及电参数为:主气流量140 L/ min、次级气比例 15% 、电流 400 A。 在射流最佳加速效应对应参数下制备的 AT40 涂层均匀致密、孔隙少。 结论 运用响应曲面法分析和解决等离子射流特性影响问题具有科学性和可操作性,能够有效指导涂层制备。
英文摘要:
      Objective To study the characteristics of the plasma jet, improve the quality of the jet, and provide support for engineering practice. Methods Using the response surface methodology, the particle velocity and temperature were used as indexes to reflect changes in the jet characteristics. Box-Behnken design (BBD) was used to analyze the influencing law of electric current, main gas flux and secondary gas proportion on the jet characteristics and the parameter interactions. Results The results indicated that the particle velocity had the greatest effect on argon flow rate,followed by electric current and secondary gas ratio. To achieve optimal heating effects of plasma jet, the gas and electrical parameters matching scheme under the nozzle were: main gas flux 80 L / min, current 450 A, secondary gas ratio 22. 5% , whereas the parameters for optimal acceleration effect were: main gas flux 140 L / min, current 400 A, secondary gas ratio 15% . The AT40 coating prepared under the corresponding parameters of the optimal jet acceleration effect was uniform and compact, with low porosity. Conclusion It is scientific and reliable to use response surface methodology to study the characteristics of the plasma jet, and it can provide effective guidance in coating preparation.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第23532372位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号