董培林.SiO2微球负载BTA缓蚀剂型自修复耐蚀涂层的制备及性能研究[J].表面技术,2016,45(3):158-163,177.
DONG Pei-lin.Preparation and properties of SiO2 microspheres loading with BTA inhibitor type self-healing corrosion coating[J].Surface Technology,2016,45(3):158-163,177 |
| SiO2微球负载BTA缓蚀剂型自修复耐蚀涂层的制备及性能研究 |
| Preparation and properties of SiO2 microspheres loading with BTA inhibitor type self-healing corrosion coating |
| 投稿时间：2015-12-04 修订日期：2016-03-20 |
| DOI：10.16490/j.cnki.issn.1001-3660.2016.03.026 |
| 中文关键词: 涂层 缓蚀剂 浸泡 多孔二氧化硅微球 阻抗 自修复 |
| 英文关键词:coating corrosion inhibitor immersion mesoporous silica impedance self-healing |
| 基金项目: |
|
|
|
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 目的 研究由负载缓蚀剂的多孔SiO2微球(SiO2)和7537聚氨酯所制备的自修复涂层的耐蚀性能和防腐机理。方法 利用负压-浸渍法将苯并三氮唑(BTA)负载到SiO2微球中；利用X射线衍射(XRD)、扫描电子显微镜(SEM)、热重分析(TGA)分别对SiO2的形貌与BTA负载含量进行分析检测；利用划痕浸泡试验、电化学极化曲线及交流阻抗技术研究SiO2、BTA以及负载有BTA的多孔SiO2微球(SiO2/BTA)对涂层耐蚀性能的影响。结果 SEM图像分析表明SiO2微球粒径约为1 μm；热重分析试验表明BTA的负载含量为32.38 wt%。划痕试验表明在浸泡的过程中除了PU+SiO2/BTA coating试样外其他试样的划痕处都出现宏观腐蚀现象；电化学极化曲线和交流阻抗结果表明PU+SiO2/BTA coating试样始终具有最低的电流密度和较高的阻抗值。结论 涂层中的多孔SiO2一方面可以储存BTA,当该涂层产生缺陷时,SiO2中的BTA被释放出来并在基体的缺陷处吸附成膜,从而使该涂层对微观缺陷具有一定的自修复功能；另一方面提高了涂层的致密性,两方面的协同作用使PU+SiO2/BTA coating试样具有最好的耐蚀性能和一定的自修复功能。 |
| 英文摘要: |
| In order to study the corrosion resistance and anti-corrosion mechanism of the self-healing coating which was prepared by adding corrosion inhibitors loaded mesoporous SiO2 microspheres into 7537 polyurethane. Method The benzotriazole (BTA) was loaded into SiO2 microspheres by negative pressure-impregnation method. The morphology and crystal structure of SiO2 microspheres and loading content of BTA were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) and thermogravimetric analysis (TGA). The effect of SiO2, BTA, SiO2-BTA addition on corrosion resistance of the coatings were studied by potentiodynamic polarization curve measurement and electrochemical impedance spectroscopy (EIS). Results SEM images showed the size of SiO2 is approximately 1 μm. TGA showed the loading content of BTA is 32.38 wt%. According to immersion test, corrosion appeared on all kinds of coatings in the progress of immersion apart from the PU SiO2/BTA coating samples. The electrochemical polarization curve and EIS results showed that PU+SiO2/BTA coating samples always has the lowest current density and higher impedance values. |