帅刚,邱骥,王红美,蔡嘉辉.铝合金 TIG 焊接接头喷射式微弧氧化腐蚀疲劳性能研究[J].表面技术,2015,44(12):110-115.
SHUAI Gang,QIU Ji,WANG Hong-mei,CAI Jia-hui.Corrosion Fatigue Properties of Aluminum Alloy TIG Welded Joint Treated by Spraying Micro-arc Oxidation[J].Surface Technology,2015,44(12):110-115
铝合金 TIG 焊接接头喷射式微弧氧化腐蚀疲劳性能研究
Corrosion Fatigue Properties of Aluminum Alloy TIG Welded Joint Treated by Spraying Micro-arc Oxidation
投稿时间:2015-09-20  修订日期:2015-12-20
DOI:10.16490/j.cnki.issn.1001-3660.2015.12.018
中文关键词:  铝合金  TIG  微弧氧化  喷射式  均匀性  腐蚀疲劳
英文关键词:aluminum alloy  TIG  micro-arc oxidation  spraying  uniformity  corrosion fatigue
基金项目:装备预先研究项目(51327040101)
作者单位
帅刚 装甲兵工程学院 装备维修与再制造工程系, 北京 100072 
邱骥 装甲兵工程学院 装备维修与再制造工程系, 北京 100072 
王红美 装甲兵工程学院 装备维修与再制造工程系, 北京 100072 
蔡嘉辉 装甲兵工程学院 装备维修与再制造工程系, 北京 100072 
AuthorInstitution
SHUAI Gang Department of Equipment Maintenance and Remanufacturing, Academy of Armored Forces Engineering, Beijing 100072, China 
QIU Ji Department of Equipment Maintenance and Remanufacturing, Academy of Armored Forces Engineering, Beijing 100072, China 
WANG Hong-mei Department of Equipment Maintenance and Remanufacturing, Academy of Armored Forces Engineering, Beijing 100072, China 
CAI Jia-hui Department of Equipment Maintenance and Remanufacturing, Academy of Armored Forces Engineering, Beijing 100072, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 研究铝合金 TIG 焊接接头经喷射式微弧氧化后对腐蚀条件下疲劳寿命的影响,为延长焊接接头的使用寿命提供一种有效的方法。 方法 采用 TIG 焊对 5083 铝合金进行焊接,观察焊接接头的组织结构,测试焊接接头的显微硬度距焊缝中心的分布情况;通过喷射式微弧氧化方法处理焊接接头,考察陶瓷层的生长曲线和截面纳米硬度;在最大载荷量为 7,8,9 kN 的条件下,分别对微弧氧化处理与未处理的焊接试样预腐蚀 168 h 后进行等幅拉伸疲劳实验,对比两种试样拉断时的循环次数。 结果 铝合金焊接接头呈现不均匀性,微弧氧化后接头陶瓷层均一性较好;陶瓷层厚度增长呈现先快后慢的趋势,表面粗糙度与厚度相关,呈近似线性增长;7,8,9 kN 的载荷下,未处理的焊接接头相比于喷射式微弧氧化的接头,疲劳寿命分别降低 50. 7% ,58. 3% ,64. 9% 。 结论 采用喷射式微弧氧化处理可改善铝合金 TIG 焊接接头的表面状态,阻隔外界腐蚀介质对焊接基体的侵蚀,提高其在预腐蚀和交变应力条件下的疲劳寿命,延长结构零件的使用寿命。
英文摘要:
      Objective To study the effect of spraying micro-arc oxidation on the corrosion fatigue life of aluminum alloy TIG welded joints, in order to provide an effective method for prolonging the life of welded joints. Methods The 5083 aluminum alloy was welded using TIG welding, the microstructure of the welded joint was observed, and the micro-hardness distribution of welded joints with the distance from the weld center was tested. The growth curve and cross-section nano-hardness of the ceramic coating were investigated after spraying MAO treatment. Under the three loading conditions with the max-stress of 7 kN,8 kN,9 kN, the tensile fatigue test was conducted for welded samples treated by micro arc-oxidation and the untreated samples after 168 h of pre-corrosion, and the fatigue life of the two samples was compared. Results The surface state of welded joints of aluminum alloy was not uniform, whereas the ceramic coating of joint showed good uniformity after micro-arc oxidation. The increment in thickness of the ceramic layer was first fast and then slow, and the surface roughness showed a nearly linear positive correlation with the thickness. Under the three loading conditions (7,8,9 kN), the fatigue life of the untreated welded joints decreased by 50. 7% ,58. 3% ,64. 9% respectively, compared with those after spraying micro-arc oxidation treatment. Conclusion The surface condition of TIG welded joints could be improved by spraying micro-arc oxidation, which blocked the erosion of weld substrate by corrosive medium, and improved the fatigue life of aluminum alloy and equipment parts under corrosion and alternating stress.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第23390665位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号