吴静沛,卢建树.低温无底釉搪瓷涂层制备及性能研究[J].表面技术,2014,43(4):130-134.
WU Jing-pei,LU Jian-shu.Preparation and Performance Study of Low Firing Non-engobe Enamel Coating[J].Surface Technology,2014,43(4):130-134
低温无底釉搪瓷涂层制备及性能研究
Preparation and Performance Study of Low Firing Non-engobe Enamel Coating
投稿时间:2014-02-18  修订日期:2014-03-28
DOI:
中文关键词:  搪瓷涂层  低温  密着性能  耐酸  烧成工艺
英文关键词:enamel coating  low temperature  adherence performance  acid tolerance  sintering technology
基金项目:
作者单位
吴静沛 浙江工业大学 材料科学与工程学院, 杭州 310014 
卢建树 浙江工业大学 材料科学与工程学院, 杭州 310014 
AuthorInstitution
WU Jing-pei College of Materials Science and Engineering, Zhejiang University of Technology, Hangzhou 310014, China 
LU Jian-shu College of Materials Science and Engineering, Zhejiang University of Technology, Hangzhou 310014, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 制备一种低温一次烧成搪瓷涂料,并研究其性能。 方法 调整搪瓷配方中耐火与助熔化合物的配比,细化搪瓷粉体粒度,采用低温长烧工艺制备搪瓷涂料。 通过 SEM 观察瓷层的微观结合形貌,考察密着性能,最后通过柠檬酸溶液处理测试其耐酸性能。 结果 最佳烧成工艺参数为:烧成温度780 ℃ ,烧结时间 8 min。 结论 涂料密着性能良好,耐酸性能良好,在保证低温烧成的情况下,搪瓷涂料具备其他良好的性能。
英文摘要:
      Objective To develop a kind of low firing non-engobe enamel and study its performance. Methods The ratio of fluxible and refractory compound was adjusted, the particle size of enamel powder was refined and the enamel coating was prepared using low-temperature long-time sintering technology. SEM was used to observe the morphology of the enamel coating and plain steel substrate to characterize its adherence. Finally, citric acid solution was used to test the acid resistance. Results The optimal parameters of enamel preparation were as follows: firing time 8 min,firing temperature 780 ℃ . Conclusion This kind of enamel coating has good acid corrosion resistance and adherence between enamel coating and plain steel substrate. In the premise of low sintering temperature, the enamel coating also had other good performance.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第23362256位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号