王英才,陈岁元,刘平平.LC4 铝合金表面硬质阳极氧化膜制备及表征[J].表面技术,2014,43(4):37-42.
WANG Ying-cai,CHEN Sui-yuan,LIU Ping-ping.Preparation and Characterization of Hard Anodic Oxidation Film on LC4 Aluminum Alloy Surface[J].Surface Technology,2014,43(4):37-42
LC4 铝合金表面硬质阳极氧化膜制备及表征
Preparation and Characterization of Hard Anodic Oxidation Film on LC4 Aluminum Alloy Surface
投稿时间:2014-03-17  修订日期:2014-06-30
DOI:
中文关键词:  LC4 铝合金  阳极氧化膜  正负脉冲波形  硬度
英文关键词:LC4 aluminum alloy  anodic oxide film  positive and negative pulse waveform  hardness
基金项目:辽宁省教育厅科学技术研究项目( LT2010031) ; 沈阳市科技工业攻关项目( F11-042-2-00)
作者单位
王英才 沈阳航天新乐股份有限责任公司, 沈阳 110004 
陈岁元 东北大学 材料各向异性与织构教育部重点实验室, 沈阳 110004 
刘平平 东北大学 材料各向异性与织构教育部重点实验室, 沈阳 110004 
AuthorInstitution
WANG Ying-cai Shenyang Hangtian Xinle Co. Ltd, Shenyang 110004, China 
CHEN Sui-yuan Key Laboratory for Anisotropy and Texture of Materials,Ministry of Education,Northeastern University, Shenyang 110004, China 
LIU Ping-ping Key Laboratory for Anisotropy and Texture of Materials,Ministry of Education,Northeastern University, Shenyang 110004, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 在 LC4 铝合金表面制备硬质阳极氧化膜,讨论工艺参数对膜层厚度和硬度的影响。 方法对阳极氧化的时间、温度、电流密度及正负脉冲电流时间比等参数进行优化实验,通过 OM,SEM,XRD 及显微硬度计等对制备的氧化膜层的厚度、硬度、形貌等进行研究。 结果 工艺优化后的参数为:温度-2 ~0 ℃ ,正脉冲电流密度 4 A / dm3,负脉冲电流密度 1 A / dm3,正负脉冲电流时间比 6 : 1 ,氧化时间 50 min。得到由一系列直径约为 50 nm 的管状单元结构组成的氧化膜,其厚度为 36 μm,硬度为 420 HV。 结论制备的阳极氧化膜具有致密的组织结构和高的硬度值。
英文摘要:
      Objective The hard anodic oxidation films were prepared on the surface of the LC4 aluminum alloy and the effects of different parameters on the thickness and hardness of the films were discussed. Methods By optimizing parameters of the anodic oxidation time, temperature, current density and the positive and negative pulse time ratio, the thickness, hardness and microstructure of the films were studied by means of OM, SEM, XRD, and hardness tester. Results The optimized parameters were: a temperature of-2 ~ 0 ℃ , a positive pulse current density of 4 A / dm3 , a negative pulse current density of 1 A / dm3 , a positive and negative pulse current time ratio of 6 : 1, and an oxidation time of 50 min. The structure of the oxide film on LC4 aluminum alloy was composed of a series of tubular cells with a diameter of 50 nm, the thickness of anodic oxidation film was 36 μm, and the hardness was 420HV. Conclusion The anodic oxidation film had fine structure and high hardness.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第24187151位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号