孟新静,周琼宇,钟庆东.阳极钝化电位对黄铜表面钝化膜半导体性能的影响[J].表面技术,2014,43(4):11-16.
MENG Xin-jing,ZHOU Qiong-yu,ZHONG Qing-dong.Semi-conducting Property of Passive Film Formed on Brass under Different Passivation Potential[J].Surface Technology,2014,43(4):11-16
阳极钝化电位对黄铜表面钝化膜半导体性能的影响
Semi-conducting Property of Passive Film Formed on Brass under Different Passivation Potential
投稿时间:2014-04-11  修订日期:2014-05-10
DOI:
中文关键词:  黄铜  钝化电位  钝化膜  半导体  Mott-Schottky 分析
英文关键词:brass  passivation potential  passive film  semiconductor  Mott-Schottky
基金项目:国家自然科学基金资助项目(50571059,50615024) ;教育部新世纪优秀人才支持计划资助项目( NCET-07-0536)
作者单位
孟新静 上海大学 上海市现代冶金与材料制备重点实验室, 上海 200072;上海电力学院 上海热交换系统节能工程技术研究中心, 上海 200090 
周琼宇 上海大学 上海市现代冶金与材料制备重点实验室, 上海 200072 
钟庆东 上海大学 上海市现代冶金与材料制备重点实验室, 上海 200072 
AuthorInstitution
MENG Xin-jing Shanghai Key Laboratory of Modern Metallurgy and Material Processing, Shanghai University, Shanghai 200072, China;Shanghai Engineering Research Center of Energy-Saving in Heat Exchange Systems,Shanghai University of Electric Power, Shanghai 200090, China 
ZHOU Qiong-yu Shanghai Key Laboratory of Modern Metallurgy and Material Processing, Shanghai University, Shanghai 200072, China 
ZHONG Qing-dong Shanghai Key Laboratory of Modern Metallurgy and Material Processing, Shanghai University, Shanghai 200072, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 研究黄铜在不同阳极钝化电位下形成的钝化膜的半导体性能。 方法 通过动电位极化曲线获取黄铜在硼酸盐缓冲溶液中的维钝电位区间,并选取 3 个钝化电位值对黄铜进行钝化处理,采用电化学阻抗谱和 Mott-Schottky 半导体理论研究阳极钝化电位对钝化膜半导体性能的影响,并进一步利用PDM 模型进行点缺陷扩散系数的计算。 结果 黄铜在硼酸盐缓冲溶液中有明显的钝化区间,不同钝化电位对应的 Mott-Schottky 直线斜率均为负值,且点缺陷扩散系数均为 10-14数量级。 随着阳极钝化电位的正移,钝化膜的阻抗值不断增加,受主密度降低,平带电位变小,空间电荷层厚度增加。 结论 黄铜在不同钝化电位下形成的钝化膜均表现出 p 型半导体的特性,膜中载流子以空穴为主,随着阳极钝化电位的正移,钝化膜的导电性能变差,耐蚀性能增强,对基体的保护作用更好。
英文摘要:
      Objective To investigate the semi-conducting property of passive films formed on brass under different passivation potential. Methods The passivation range of brass in borate buffer solution was obtained by potentiodynamic polarization curves, and three passivation potentials were chosen. The electrochemical impedance spectroscopy and Mott-Schottky theory were used,and the diffusion coefficient of passive film was calculated using PDM. Results The brass showed obvious passivation state in borate buffer solution. The Mott-Schottky plots were linear with a negative slop. With the passivation potential moving towards positive, the film impedance increased, the acceptor density and the flat potential decreased, the space charge layer thickness increased, and the order of magnitude of point defect diffusion coefficient was 10-14. Conclusion Under different passivation potential, the passive films on the brass surface showed the property of p-type semiconductor, the majority of the carriers in the passive film were holes. With the passivation potential moving towards positive, the conductivity of the film decreased and the corrosion resistance was improved, resulting in better protection.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第24203163位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号