王云英,陈玉如,孟江燕,孙旭.低温等离子体处理条件对低密度聚乙烯薄膜表面性能的影响[J].表面技术,2013,42(6):55-58,82.
WANG Yun-ying,CHEN Yu-ru,MENG Jiang-yan,SUN Xu.Effect of Low Temperature Plasma Treatment on the Surface Properties of LDPE Film[J].Surface Technology,2013,42(6):55-58,82
低温等离子体处理条件对低密度聚乙烯薄膜表面性能的影响
Effect of Low Temperature Plasma Treatment on the Surface Properties of LDPE Film
投稿时间:2013-07-12  修订日期:2013-08-20
DOI:
中文关键词:  低密度聚乙烯  低温等离子体处理  改性  剥离强度
英文关键词:low density polyethylene  low-temperature plasma treatment  modification  peel strength
基金项目:航空科学基金(20120956005)
作者单位
王云英 无损检测技术教育部重点实验室( 南昌航空大学) , 南昌 330063 
陈玉如 无损检测技术教育部重点实验室( 南昌航空大学) , 南昌 330063 
孟江燕 无损检测技术教育部重点实验室( 南昌航空大学) , 南昌 330063 
孙旭 无损检测技术教育部重点实验室( 南昌航空大学) , 南昌 330063 
AuthorInstitution
WANG Yun-ying Key laboratory of NDT ( Nanchang Hangkong University) , the Ministry of Education, Nanchang 330063, China 
CHEN Yu-ru Key laboratory of NDT ( Nanchang Hangkong University) , the Ministry of Education, Nanchang 330063, China 
MENG Jiang-yan Key laboratory of NDT ( Nanchang Hangkong University) , the Ministry of Education, Nanchang 330063, China 
SUN Xu Key laboratory of NDT ( Nanchang Hangkong University) , the Ministry of Education, Nanchang 330063, China 
摘要点击次数:
全文下载次数:
中文摘要:
      目的 研究低密度聚乙烯( LDPE) 薄膜经低温等离子体处理前后,表面性能的变化情况。 方法 采用不同的处理条件,对 LDPE 进行低温等离子体处理,并对比 LDPE 薄膜处理前后的表面形貌、表面接触角及剥离强度。 结果 采用空气为处理气氛时,在功率 44 W、真空度 60 Pa 的条件下处理 30 s,LDPE薄膜的静态接触角从处理前的 101 o 降到 13 . 5 o ;等离子体处理后的 LDPE 薄膜在 1 h 内,接触角会迅速上升到 74 o ,失去等离子体处理的效果。 结论 对于处理气氛,空气比 N2 和 CO2 的处理效果更好;等离子体处理后的 LDPE 薄膜具有明显的时效性,应立即进入下道工序。
英文摘要:
      Objective To study the change of the surface properties of low-density polyethylene ( LDPE ) film treated by low-temperature plasma. Methods The LDPE film was treated by low-temperature plasma under different treating conditions to compare the surface morphology, surface contact angle and peel strength of the LDPE film before and after treatment . Results Treating LDPE film using air as treatment atmosphere with 44 W, 30 s, 60 Pa parameters decreased its static contact angle from 101 o to 13 . 5 o . The contact angle of LDPE film quickly rose to 74 o within one hour after low-temperature plasma treatment and lost the plasma treatment effect . Conclusion The air was a better treatment atmosphere than N2 and CO2 . The timeliness of plasma treated LDPE film was obvious and should enter the next process immediately after low-temperature plasma treatment .
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第23446558位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号