王彦峰,李争显,华云峰,王宝云,杜继红.C 掺杂方式对 TiAlSiN 膜层组织及性能的影响[J].表面技术,2013,42(4):32-34,38.
WANG Yan-feng,LI Zheng-xian,HUA Yun-feng,WANG Bao-yun,DU Ji-hong.Influence of C Incorporation Modes on the TiAlSiN Coating' s Microstructure and Properties[J].Surface Technology,2013,42(4):32-34,38 |
| C 掺杂方式对 TiAlSiN 膜层组织及性能的影响 |
| Influence of C Incorporation Modes on the TiAlSiN Coating' s Microstructure and Properties |
| 投稿时间：2013-04-26 修订日期：2013-05-20 |
| DOI： |
| 中文关键词: C 掺杂 TiAlSiN 硬质膜层 显微组织 摩擦性能 |
| 英文关键词:C incorporatin TiAlSiN hard coating microstructure wearing properties |
| 基金项目: |
| 作者 | 单位 |
| 王彦峰 | 西北有色金属研究院, 西安 710016 |
| 李争显 | 西北有色金属研究院, 西安 710016 |
| 华云峰 | 西北有色金属研究院, 西安 710016 |
| 王宝云 | 西北有色金属研究院, 西安 710016 |
| 杜继红 | 西北有色金属研究院, 西安 710016 |
|
| Author | Institution |
| WANG Yan-feng | Northwest Institute for Nonferrous Metal Research, Xi'an 710016 , China |
| LI Zheng-xian | Northwest Institute for Nonferrous Metal Research, Xi'an 710016 , China |
| HUA Yun-feng | Northwest Institute for Nonferrous Metal Research, Xi'an 710016 , China |
| WANG Bao-yun | Northwest Institute for Nonferrous Metal Research, Xi'an 710016 , China |
| DU Ji-hong | Northwest Institute for Nonferrous Metal Research, Xi'an 710016 , China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 采用电弧离子镀与磁控溅射联合沉积技术,以不同的 C 掺杂方式在高速钢基体表面制备了 C /TiAlSiN 多元复合硬质膜层,对膜层的成分、组织结构、显微硬度及摩擦磨损性能进行了表征,并与相同条件下制备的未掺杂 TiAlSiN 膜进行了对比。 结果表明,不同的掺杂方式使得膜层的组织与性能不同,在 TiAlSiN 硬质膜层的制备过程中实施 C 掺杂,能够显著优化该膜层体系的组织结构及显微硬度,并大大改善其摩擦磨损性能。 |
| 英文摘要: |
| A combination of arc and magnetron sputtering deposition technology was used to synthesize the C / TiAlSiN hard coatings with different C incorporation modes on the high-speed steel substrates. The coating ' s composition, microstructure, microhardness and wearing properties were studied and compared with that of TiAlSiN coatings which has none-C incorporation. It was found that the coatings had different microstructure and properties with different C incorporation mode. The incorporation of C during the TiAlSiN coating synthesis was very useful to optimize the coating's microstructure and micro hardness,and also good for its wearing properties. |