吴行阳,黄夏婧,张建华.非晶碳基薄膜及其表面织构化后的水润滑性能研究进展[J].表面技术,2012,(4):87-90,121.
WU Xing-yang,HUANG Xia-jing,ZHANG Jian-hua.Progress in Water Lubrication of Amorphous Carbon Films and Surface Texturing[J].Surface Technology,2012,(4):87-90,121
非晶碳基薄膜及其表面织构化后的水润滑性能研究进展
Progress in Water Lubrication of Amorphous Carbon Films and Surface Texturing
投稿时间:2012-03-26  修订日期:2012-08-20
DOI:
中文关键词:  水润滑  类金刚石膜  摩擦化学  表面织构
英文关键词:water lubrication  diamond-like carbon  tribochemistry  surface texturing
基金项目:国家自然科学基金(51075250)
作者单位
吴行阳 上海大学机电工程与自动化学院,上海200072 
黄夏婧 上海大学机电工程与自动化学院,上海200072 
张建华 上海大学机电工程与自动化学院,上海200072 
AuthorInstitution
WU Xing-yang School of Mechatronics Engineering and Automation, Shanghai University, Shanghai 200072, China 
HUANG Xia-jing School of Mechatronics Engineering and Automation, Shanghai University, Shanghai 200072, China 
ZHANG Jian-hua School of Mechatronics Engineering and Automation, Shanghai University, Shanghai 200072, China 
摘要点击次数:
全文下载次数:
中文摘要:
      非晶碳基薄膜在水中具有低摩擦磨损特性和好的耐腐蚀性,但在摩擦过程中容易发生局部剥落,进一步提高薄膜在水中的承载力是目前的热点研究方向之一。在综合分析非晶碳基薄膜的摩擦学性能及其改性,以及采用表面织构化提高材料承载力的基础上,阐述了将两者相结合以改善薄膜整体性能的研究现状和发展前景。
英文摘要:
      Amorphous carbon films possess excellent tribological properties and corrosion resistance. However, the films are easy to peel off the substrates partially during the sliding process under water-lubricated conditions. The current research on this issue is focused on improving the load-carrying capability of the films. The tribological properties and the progress in enhancing adhesion of the films, as well as the effect of surfacet exturing on the load carrying capability of materials were expounded. The future prospect of combining the coating and surface-texturing technologies to improving the tribology behavior of the films was discussed.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第23360980位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号