冶艳,尚魁平,鲍明东,徐雪波,葛培林,江利.CrN 硬质镀层对磨热固性塑料的摩擦学行为研究[J].表面技术,2012,(1):27-29,36.
YE Yan,SHANG Kui-ping,BAO Ming-dong,XU Xue-bo,GE Pei-lin,JIANG Li.Study on Tribological Behavior of CrN Hard Film Against Thermosetting Plastics[J].Surface Technology,2012,(1):27-29,36
CrN 硬质镀层对磨热固性塑料的摩擦学行为研究
Study on Tribological Behavior of CrN Hard Film Against Thermosetting Plastics
投稿时间:2011-09-23  修订日期:2012-02-20
DOI:
中文关键词:  CrN 硬质薄膜  热固性塑料  摩擦系数  磨损
英文关键词:CrN hard film  thermosetting plastis  friction coefficient  wear
基金项目:
作者单位
冶艳 中国矿业大学材料科学与工程学院,徐州221008 
尚魁平 中国矿业大学材料科学与工程学院,徐州221008 
鲍明东 宁波工程学院材料工程研究所,宁波315016 
徐雪波 宁波工程学院材料工程研究所,宁波315016 
葛培林 宁波工程学院材料工程研究所,宁波315016 
江利 中国矿业大学材料科学与工程学院,徐州221008 
AuthorInstitution
YE Yan School of Material Science and Technology, China University of Mining and Technology, Xuzhou221008,China 
SHANG Kui-ping School of Material Science and Technology, China University of Mining and Technology, Xuzhou221008,China 
BAO Ming-dong Institute of Materials Engineering,Ningbo University of Technology,Ningbo 315016, China 
XU Xue-bo Institute of Materials Engineering,Ningbo University of Technology,Ningbo 315016, China 
GE Pei-lin Institute of Materials Engineering,Ningbo University of Technology,Ningbo 315016, China 
JIANG Li School of Material Science and Technology, China University of Mining and Technology, Xuzhou221008,China 
摘要点击次数:
全文下载次数:
中文摘要:
      采用封闭非平衡磁控溅射法制备了CrN 硬质镀层,以热固性塑料PA66和ABS为其中一个摩擦副,在Pin-on-disc磨损试验机上测试了对磨CrN 硬质镀层和M42高速钢时的摩擦系数。应用立体显微镜和扫描电子显微镜对摩擦副表面磨损轨迹的微观形貌及磨屑进行了观察和分析。结果表明:CrN 硬质薄膜与M42高速钢对磨PA66和ABS塑料时,CrN 硬质薄膜的摩擦系数要比高速钢小,而且数值稳定;塑料直接与高速钢对磨的摩擦系数波动较大。
英文摘要:
      CrN hard coatings were deposited onto steel substrate using closed unbalanced field magnetron sputterion plating system. Friction coefficient of CrN hard coatings and M42 high speed steel(HSS)against plastics(PA66,ABS) were investigated using Pin-on-disc tester. The microstructures of worn surfaces and wear debris of CrN films were observed using SEM and stereomocroscope. The results show that the friction coefficient of CrN hard coatings is smaller and more stable than that of M42 HSS when wearing against plastics(PA66,ABS). The friction coefficient is unstable when the plastics direct wear the high-speed steel.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第23707641位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号