庞国星,陈志勇,李忠磊,黄胜洲.氧化时间对硬铝合金硬质阳极氧化膜性能的影响[J].表面技术,2010,39(6):87-89,103.
PANG Guo-xing,CHEN Zhi-yong,LI Zhong-lei,HUANG Sheng-zhou.The Effect of Oxidation Time on Property of Hard Anodic Oxidation Film on Hard Aluminum Alloy[J].Surface Technology,2010,39(6):87-89,103 |
| 氧化时间对硬铝合金硬质阳极氧化膜性能的影响 |
| The Effect of Oxidation Time on Property of Hard Anodic Oxidation Film on Hard Aluminum Alloy |
| 投稿时间：2010-08-20 修订日期：2010-12-10 |
| DOI： |
| 中文关键词: 硬铝合金 硬质阳极氧化 氧化时间 性能 |
| 英文关键词:hard aluminum alloy hard anodic oxidation oxidation time property |
| 基金项目:北华航天工业学院“材料加工工程重点发展学科”资助项目(XK-2010-05-Z) |
|
|
| Author | Institution |
| PANG Guo-xing | Department of Material Engineering, North China Institute of Astronautic Engineering, Langfang 065000, China |
| CHEN Zhi-yong | Department of Material Engineering, North China Institute of Astronautic Engineering, Langfang 065000, China |
| LI Zhong-lei | Department of Material Engineering, North China Institute of Astronautic Engineering, Langfang 065000, China |
| HUANG Sheng-zhou | Department of Material Engineering, North China Institute of Astronautic Engineering, Langfang 065000, China |
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 改变氧化时间,在硬铝合金表面制备硬质阳极氧化膜,研究了氧化时间对硬质阳极氧化膜厚度、硬度和封孔处理后耐腐蚀性能的影响,并采用金相显微镜和扫描电子显微镜分析了氧化膜的表面形貌。结果表明:所得硬质阳极氧化膜具有类似蜂窝状的结构,氧化时间以60 min为宜,氧化60 min所得的氧化膜综合性能最佳。 |
| 英文摘要: |
| Through changing oxidation time, the hard anodic oxidation film on hard Aluminum alloy was made, and the effect on film thickness, film hardness, film anti-corrosion after sealing treatment was researched with different oxidation time, and the surface appearance was analyzed with microscope and SEM. Results indicate that the obtained hard anodic oxidation film is with alike honeycomb structure, the suitable oxidation time is 60 min. Oxidation film made with 60 min oxidation time is with the optimum comprehensive properties. |