郑龙,熊英,程涛.电镀/化学镀双层镍的研究[J].表面技术,2010,39(6):16-17,62.
ZHENG Long,XIONG Ying,CHENG Tao.Study on Electroplating Nickel Add Electroless Ni-P Plating[J].Surface Technology,2010,39(6):16-17,62 |
| 电镀/化学镀双层镍的研究 |
| Study on Electroplating Nickel Add Electroless Ni-P Plating |
| 投稿时间：2010-10-14 修订日期：2010-12-10 |
| DOI： |
| 中文关键词: 电镀镍 化学镀Ni-P合金 双层镍 耐蚀性 结合强度 |
| 英文关键词:electroplating nickel electroless Ni-P plating two layer nickel corrosion resistance combine strength |
| 基金项目: |
|
|
|
|
| 摘要点击次数: |
| 全文下载次数: |
| 中文摘要: |
| 在45#钢表面先电镀高硫镍,再化学镀Ni-P合金镀层获得电镀/化学镀双层镍,并制备了单一化学镀Ni-P合金层进行对比。采用中性盐水、酸性盐水和浓盐酸浸泡实验考查了镀层的耐蚀性能,采用热震实验和锉刀实验考查了镀层的结合强度,并分析了镀层的表面形貌和硬度。结果表明:电镀/化学镀双层镍在较薄时就具有与单层Ni-P合金镀镍层相当的耐蚀性能,且与钢基体结合良好。 |
| 英文摘要: |
| The electroplating/electroless plating's two layers nickel on the 45# steel surface was obtained by electroless Ni-P plating after electroplating high sulphur nickel. It was compared with the single electroless Ni-P plating. Two layer nickel's corrosion resistance was investigated with the experiments of neutral brine, the acidity brine and thick hydrochloric soaks. Two layer nickel's combine strength was studied with the experiments of hot vibration test and file test,and it's surface morphology and hardness were analyzed.The experimental results show that the thinner two layers nickelis as the corrosion resistance as electroless Ni-P plating.it is good that the two layers nickel combine with the steel. |