侯国梁,周惠娣,安宇龙,赵晓琴,刘光.铝合金异形曲面热喷涂涂层的制备及性能研究[J].表面技术,2010,39(3):67-70.
HOU Guo-liang,ZHOU Hui-di,AN Yu-long,ZHAO Xiao-qin,LIU Guang.Study on Preparation and Performance of Thermal Spraying Coatings onto Aluminum Alloy Abnormity Bent Surface[J].Surface Technology,2010,39(3):67-70
铝合金异形曲面热喷涂涂层的制备及性能研究
Study on Preparation and Performance of Thermal Spraying Coatings onto Aluminum Alloy Abnormity Bent Surface
  修订日期:2010-06-10
DOI:
中文关键词:  HVOF  APS  热喷涂涂层  异形曲面
英文关键词:HVOF  APS  thermal spraying coatings  abnormal bent surface
基金项目:国家自然科学基金委创新研究群体科学基金资助项目(50421502);国家973计划资助项目(2007CB607601);中国科学院“西部之光”人才培养计划“西部博士资助”项目(2007-12-18)
作者单位
侯国梁 1.中科院兰州化学物理研究所固体润滑国家重点实验室,兰州730000;2.中科院北京研究生院,北京100049 
周惠娣 中科院兰州化学物理研究所固体润滑国家重点实验室,兰州730000 
安宇龙 1.中科院兰州化学物理研究所固体润滑国家重点实验室,兰州730000;2.中科院北京研究生院,北京100049 
赵晓琴 中科院兰州化学物理研究所固体润滑国家重点实验室,兰州730000 
刘光 1.中科院兰州化学物理研究所固体润滑国家重点实验室,兰州730000;2.中科院北京研究生院,北京100049 
AuthorInstitution
HOU Guo-liang 1.State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics,Chinese Academy of Sciences, Lanzhou 730000, China;2.Graduate School of Chinese Academy of Science, Beijing 100049, China 
ZHOU Hui-di State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics,Chinese Academy of Sciences, Lanzhou 730000, China 
AN Yu-long 1.State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics,Chinese Academy of Sciences, Lanzhou 730000, China;2.Graduate School of Chinese Academy of Science, Beijing 100049, China 
ZHAO Xiao-qin State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics,Chinese Academy of Sciences, Lanzhou 730000, China 
LIU Guang 1.State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics,Chinese Academy of Sciences, Lanzhou 730000, China;2.Graduate School of Chinese Academy of Science, Beijing 100049, China 
摘要点击次数:
全文下载次数:
中文摘要:
      采用大气等离子喷涂(APS)(液态CO2气化冷却和未冷却)和超音速火焰喷涂(HVOF),在模拟加力泵涡壳的异形铝合金工件内曲面,制备了耐气蚀性较好的3种涂层,并考察涂层和异形曲面基体的结合情况及涂层的相组成、显微硬度和孔隙率。结果表明:HVOF在其焰流无法垂直喷涂的部位涂层与基体结合较差;未使用CO2冷却的APS涂层卷曲,涂层中有明显裂纹;使用CO2冷却的APS涂层与基体结合良好,涂层中没有裂纹,该工艺是目前在铝合金异形曲面制备热喷涂涂层的有效途径。
英文摘要:
      Three types coating that had fine cavitaion erosion resistance,derived from NiCr feedstock,were fabricated on abnormity bent surface of aluminum alloy workpieces using air plasma spraying(APS)with and without cooling by gasified CO2and high velocity oxy-fuel(HVOF). The combination between coatings and substrate, and the composition, microharness and porosity of the coatings were reviewed. The obtained results shows that HVOF sprayed coating has bad combination with substrate where the flame can't vertically sprayed on; APS sprayed coating without cooling by gasified CO2curls and has distinct crack; APS sprayed coating cooled by gasified CO2has good combination with substrate in anyplace and has not crack. It can be concluded that APS is an effective method to produce functional coatings on aluminum abnormal bent surface at present.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第23609472位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号