巩运兰,杨云,王为,郭鹤桐.不同电解温度下阳极氧化铝薄膜纳米孔的自组织过程[J].表面技术,2008,37(5):1-4.
GONG Yun-Ian,YANG Yun,WANG Wei,GUO He-tong.Self-organized Process of the Anodic Alumina Films at the Different Temperatures[J].Surface Technology,2008,37(5):1-4
不同电解温度下阳极氧化铝薄膜纳米孔的自组织过程
Self-organized Process of the Anodic Alumina Films at the Different Temperatures
投稿时间:2008-06-27  修订日期:2008-10-10
DOI:
中文关键词:  阳极氧化  氧化铝薄膜  温度  自组织过程  纳米孔
英文关键词:Anode oxidation  Anodic alumina films  Temperature  Self-organized process  Nanoporous
基金项目:天津市自然科学资金资助项目( 06YFJMIC11400)
作者单位
巩运兰 天津商业大学,天津300134 
杨云 天津商业大学,天津300134 
王为 天津大学化工学院,天津300072 
郭鹤桐 天津大学化工学院,天津300072 
AuthorInstitution
GONG Yun-Ian Tianjin University of Commerce, Tianjin 300134, China 
YANG Yun Tianjin University of Commerce, Tianjin 300134, China 
WANG Wei School of Chemical Engineering of Tianjin University, Tianjin 300072, China 
GUO He-tong School of Chemical Engineering of Tianjin University, Tianjin 300072, China 
摘要点击次数:
全文下载次数:
中文摘要:
      研究温度对阳极氧化铝薄膜纳米孔自组织过程的影响。使用环境扫描电镜( ESEM)研究了铝试样在硫酸、草酸、磷酸溶液中,于不同电解温度下阳极氧化形成的氧化铝薄膜形貌。通过分析阳极氧化时电流密度与时间关系曲线,研究了温度对阳极氧化铝薄膜纳米孔自组织过程的影响。提出降低电解温度能够缩短纳米孔自组织过程的时间,是由于降低电解温度增大了纳米孔内表面的表面张力。并且提出在不同的电解质溶液中,电解温度对纳米孔自组织过程的影响程度不同,电解温度对纳米孔自组织过程的影响以在硫酸溶液中最敏感,草酸次之,在磷酸溶液中的影响最小。
英文摘要:
      The appearance of the anodic alumina films formed in H2S04,H2C204 and H3P04 solution at different temperatures was studied by ESEM. The effect of the temperature of the electrolytes on the self-organized process of anodic alumina film was researched by analyzing the relation of the anodic current density and oxidation time in H2S04, H2C204 and H3P04 solution at different temperatures. The results show that the surface tension in the nanoporous internal face are increased with the decrease in electrolysis temperature, the complete time of the self-organized process of the anodic alumina film can be shortened by lowering temperature. But the degree of temperature influence on the self-organized process of anodic alumina film is different in the different electrolytes. The higher the degree of the temperature influence on the stable current density, the greater change the reaction heat has, the more difference of the surface tension in the nanoporous face and, the more distinct the effect of the temperature on the self-organized process of anodic alumina film. The effect of the temperature on the self-organized process of anodic alumina film is consistent with it on the stable current density and on the nanoporous aperture. The effect of the temperature on the self-organized process of anodic alumina film is decided by the nanoporous aperture depend on temperature. The effect of the temperature on the self-organized process of anodic alumina film indifferent solutions is in following order: H2S04 > H2C204 > H3P04
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第23445054位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号