李艳红,陈宏书,郑建龙,张五龙,王结良,陈卫星.环氧导静电涂料固化剂的研究[J].表面技术,2008,37(4):35-36,80.
LI Yan-hong,CHEN Hong-shu,ZHENG Jian-long,ZHANG Wu-long,WANG Jie-liang,CHEN Wei-xing.Study on the Curing Agents for the Epoxy Static Electricity Conductive Coating[J].Surface Technology,2008,37(4):35-36,80
环氧导静电涂料固化剂的研究
Study on the Curing Agents for the Epoxy Static Electricity Conductive Coating
投稿时间:2008-05-19  修订日期:2008-08-10
DOI:
中文关键词:  环氧导静电涂料  固化剂  酚醛胺T31  聚酰胺650
英文关键词:Epoxy static electricity conductive coating  Curing agent  Phenolic aldehyde amine T31  Polyimide 650
基金项目:
作者单位
李艳红 西安工业大学材料与化工学院,陕西西安710032 
陈宏书 总后建筑工程研究所,陕西西安710032 
郑建龙 总后建筑工程研究所,陕西西安710032 
张五龙 总后建筑工程研究所,陕西西安710032 
王结良 总后建筑工程研究所,陕西西安710032 
陈卫星 西安工业大学材料与化工学院,陕西西安710032 
AuthorInstitution
LI Yan-hong School of Materials and Chemical Engineering, Xian Technological University, Xian 710032, China 
CHEN Hong-shu Architectural Engineering Institute of General Logistics Department, Xian 710032, China 
ZHENG Jian-long Architectural Engineering Institute of General Logistics Department, Xian 710032, China 
ZHANG Wu-long Architectural Engineering Institute of General Logistics Department, Xian 710032, China 
WANG Jie-liang Architectural Engineering Institute of General Logistics Department, Xian 710032, China 
CHEN Wei-xing School of Materials and Chemical Engineering, Xian Technological University, Xian 710032, China 
摘要点击次数:
全文下载次数:
中文摘要:
      固化剂的种类对环氧导静电涂料的各项性能影响很大,因此,固化剂的选择尤为重要。对酚醛胺T31、聚酰胺650两种固化剂进行比较试验,并对涂膜的力学性能(漆膜干燥时间、抗冲击强度、附着力、柔韧性)、导静电性能、耐油性能进行研究。结果表明:与聚酰胺650相比,酚醛胺T31配制的环氧导静电涂料具有优良的力学性能和耐油性能,且表面电阻率为l0 8Ω,而聚酰胺650配制的涂料表面电阻率为lO 11 Ω。因此,酚醛胺T31是环氧导静电涂料的最佳固化剂。
英文摘要:
      It is very important to choose the curing agent in coatings, the type of curing agents has considerable influence on diversified properties of coating. The two curing agents ( phenolic aldehyde amine T31 and polyimide 650 ) were compared. The influence of curing agents on the properties of coating, such as mechanics capability( drying time . ash strength, adhesion and flexility, static conductivity capability and oil-resistant capability were also studied. It was found that T31 as curing agents for coating has outstanding mechanics capability and oil-resistant capability and surface resistance rate is l0 8 Ω , whereas 650 is 10 11 Ω. So T31 is optimal curing agents for the epoxy static electricity conductive coating.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第23444831位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号