黄成群,吴世学,高家诚.铜包铁粉末表面的钝化处理[J].表面技术,2007,36(5):41-42,74.
HUANG Cheng-qun,YVU Shi-xue,GAO Jia-cheng.Surface Passivation of Copper Cladded Iron Powder[J].Surface Technology,2007,36(5):41-42,74
铜包铁粉末表面的钝化处理
Surface Passivation of Copper Cladded Iron Powder
投稿时间:2007-07-24  修订日期:2007-10-10
DOI:
中文关键词:    包覆粉末  钝化
英文关键词:Copper  Cladding powder  Passivation
基金项目:
作者单位
黄成群 重庆电力高等专科学校,重庆400053 
吴世学 重庆电力高等专科学校,重庆400053 
高家诚 重庆大学材料科学与工程学院,重庆400030 
AuthorInstitution
HUANG Cheng-qun Chongqing Electric Powder College, Chongqing 400053, China 
YVU Shi-xue Chongqing Electric Powder College, Chongqing 400053, China 
GAO Jia-cheng College of Materials Science and Engineering, Chongqing University, Chongqing 400030, China 
摘要点击次数:
全文下载次数:
中文摘要:
      通过对2种苯并三氮唑(BTA)有机添加剂复合配方和1种常用的钝化剂对比试验,探索了BTA系复配钝化剂在铜包铁粉末防变色钝化处理中的钝化效果及机理,通过硝酸滴定试验、氨水滴定试验、S0:加速腐蚀试验、大气腐蚀试验及温湿耐蚀试验,得出铜包铁粉末表面钝化的最佳工艺为:0. 50-/0 BTA,l - 3g/L OP-IO,温度为50 - 600C,处理时间为3-5 min。BTA复配体系处理后的防护效果好于BTA单一体系,单一BTA处理后的钝化效果好于目前常用的钾肥皂钝化效果。
英文摘要:
      Through contrast test of a common passivating agent and two compounding recipes included BTA and organic addition agent, the effectiveness and mechanics of passivating on the compound passivating agent to protect copper cladding from being oxidized were studied. By means of nitric acid titration test, ammonia liquor titration test, S02 accelerating corrosion test, atmospheric exposure test and temperature-moisture anticorrosion test, we can get that the effect of BTA-OP-10 0n cladding is better than other passivants. The best dosages added is BTA 0. 50-/o , OP-10 1 -3 g/ L, temperature of the process is 50 ~ 60℃ and the processing time is 3-5min. Meanwhile, the effect of corrosion resistant of compounding recipe included BTA and organic addition agent is better than that of only including BTA, the effect of corrosion resistant of only including BTA is better than that of kalium soap used in these days.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第23706725位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号