段关文,李金富,王拥军,徐志雄.铝合金的微弧氧化研究[J].表面技术,2007,36(3):30-33.
DUAN Guan-wen,LI Jin-fu,WANG Yong-jun,XU Zhi-xiong.Research of Micro-arc Oxidation of Aluminum Alloy[J].Surface Technology,2007,36(3):30-33
铝合金的微弧氧化研究
Research of Micro-arc Oxidation of Aluminum Alloy
投稿时间:2007-02-05  修订日期:2007-06-10
DOI:
中文关键词:  铝合金  微弧氧化  陶瓷膜层  α-A12 03  γ-Al2 03
英文关键词:Aluminum alloy  Micro-arc oxidation  Ceramic coating  α-Al203  γ-Al203
基金项目:
作者单位
段关文 中国兵器工业第52研究所烟台分所,山东烟台264003 
李金富 中国兵器工业第52研究所烟台分所,山东烟台264003 
王拥军 中国兵器工业第52研究所烟台分所,山东烟台264003 
徐志雄 中国兵器工业第52研究所烟台分所,山东烟台264003 
AuthorInstitution
DUAN Guan-wen Yantai Branch of No. 52 Institute of China Ordnance Industry, Yantai 264003 , China 
LI Jin-fu Yantai Branch of No. 52 Institute of China Ordnance Industry, Yantai 264003 , China 
WANG Yong-jun Yantai Branch of No. 52 Institute of China Ordnance Industry, Yantai 264003 , China 
XU Zhi-xiong Yantai Branch of No. 52 Institute of China Ordnance Industry, Yantai 264003 , China 
摘要点击次数:
全文下载次数:
中文摘要:
      在硅酸钠和氢氧化钠电解液中利用微弧氧化技术在LY12铝合金表面生成陶瓷膜层。对膜层进行了SEM和TEM观察。对微弧氧化过程中电参数的变化规律进行了探讨,并分析了电参数对微弧氧化的影响。结果表明:在本实验条件下,用微弧氧化工艺在铝合金表面可制得致密的、厚度迭200 pcm的氧化膜,膜层与铝基体的结合层形成了纳米晶相。电参数对陶瓷层的厚度、硬度、粗糙度都有较大的影响。对微弧氧化膜层的钢球和陶瓷球磨损的对比可知,与钢球的磨损主要是粘着磨损,对陶瓷球的磨损主要是磨料磨损。
英文摘要:
      Ceramic coating was obtained by micro-arc oxidation on LY12 aluminum alloy in sodium silicate and sodium hydroxide electrolyte, and examined by SEM and TEM. The regulations of current and voltage were studied. Results show that a compact ceramic coating with thickness of 200p4m is obtained by micro-arc oxidation on Al surface, nano-crystalloid emerges in the joint that lies between the coating and Al. The results show that both the voltage and the current play very important roles in the thickness, hardness and surface roughness of the ceramic coating. Comparing the ceramic coating attrition tested by steel ball and ceramic ball, the attrition with the steel ball is adhesion attrition, and the attrition with ceramic ball is abrasive attrition.
查看全文  查看/发表评论  下载PDF阅读器
关闭

关于我们 | 联系我们 | 投诉建议 | 隐私保护 | 用户协议

您是第23445120位访问者    渝ICP备15012534号-3

版权所有:《表面技术》编辑部 2014 surface-techj.com, All Rights Reserved

邮编:400039 电话:023-68792193传真:023-68792396 Email: bmjs@surface-techj.com

渝公网安备 50010702501715号